ORASTICK - fluorescent orange - 60 x 100 cm
To ensure optimal product properties, ORASTICK® is manufactured exclusively from virgin polyester granules, not recycled material.
ORACOVER® and ORASTICK® have identical properties and can be used interchangeably. The fundamental difference between these two products lies in the adhesive layer.
While ORACOVER® features a heat-activated adhesive, ORASTICK® has a self-adhesive, permanent adhesive. This difference also affects the application technique. Due to its self-adhesive backing, ORASTICK® can be applied significantly faster than ORACOVER®.
ORASTICK® is positioned on the surface to be covered, the edges are ironed, and the remaining surface is heated with a hot air gun, shrinking and bonding. During this process, the hot film is pressed into its final position using our ORACOVER® / ORATEX® felt squeegee (No. 0915 or 0948), where it is anchored by the adhesive.
ORASTICK® is positioned on the surface to be covered, the edges are ironed, and the remaining area is heated with a hot air gun, shrinking and bonding. Due to its self-adhesive properties, ORASTICK® film is also ideal for covering models made of rigid foam. With the exception of transparent colors, ORASTICK® is available in all ORACOVER® colors. ORASTICK® can be painted over with all ORACOLOR® paints.
ORASTICK® is compatible with all ORACOLOR® paints.
Features:
• Iron-on
• Hair dryer compatible
• Self-adhesive backing
Technical specifications:
Lengths: 1 m (cut from the roll according to order)
Width: 60 cm
• Polyester film with colored and permanent adhesive coating
• Material thickness: approx. 45 - approx. 65 μm
• Backing film: 23 μm
• Weight: approx. 57 - approx. 109 g/m² (depending on color)
• Tensile strength (longitudinal & transverse): min. 283 N / 50 mm
• Elongation at break (longitudinal & transverse): min. 90%
• Shrinkage: min. 5% biaxial (referenced to 150 °C)
• Melting point: 250 °C
• Adhesive strength: min. 10 N / 25 mm